Study on structural characterization of hexamolybdocobaltate(III) pyridine-3-carboxylic acid (H3O)3[СoMО6O18(OH)6].(С6H5NO2)2.5Н2О
253 viewsDOI:
https://doi.org/10.54939/1859-1043.j.mst.81.2022.86-91Keywords:
Heteropolyanion; X-ray crystallography; IR; NMR.Abstract
The hexamolybdocobaltate(III) pyridine-3-carboxylic acid (H3O)3[СОMО6O18(OH)6] .(С6H5NO2)2.5Н2О(compound 1) is an organic-inorganic hybrid material with a three-tilt crystal system belonged to space group P-1. This compound is a promising candidate for applications in the field of pharmaceutical chemistry and catalysis. Compound 1 was synthesized by the hydrothermal method. The prepared compound 1 was characterized by structural characteristics that were studied by methods: X-ray crystallography (XRC), NMR, and IR spectroscopies. The unit cell parameters of compound 1 were determined to be: a = 9.230 Å, b = 10.700 Å, с = 10.850 Å, α = 95.95о, β = 110.01°, γ = 105.11°, V = 949.9 Å3, and ρ = 2.479 g/cm3, Z = 1.
References
[1]. Pope, M.T. “Heteropoly and Isopoly oxometalates, (Inorganic Chemistry), Spinger-Verlag Berlin Heidelberg. Поп М. С. Гетерополи– и изополиоксометаллаты / перевод с англ. под ред. Э. Н. Юрченко” Новосибирск: Наука, 232 с, (1990).
[2]. Порай – Кощиц М.А., Сергиенко В.С., Юрченко Э.Н. Журнал структ. химии, 27(1), 187-188, (1986).
[3]. Сергиенко В.С., Порай-Кошиц М.А. “Кристаллоструктурный аспект строения изополи- и гетерополисоединений”. Итоги науки техники, сер. кристаллохимия. Т.19. ВИНИТИ, М., с. 79-147, (1955).
[4]. Никитина Е. А. “Гетерополисоединения”. М.: Госхимиздат, 424 с, (1962).
[5]. Добрынина Н.А. “Изополи- и гетерополисоединения”. Ж. неорган. химии, Т.47, №4, 2002, с.577.
[6]. Gumerova N.I., Caldera Fraile T., Roller A., Giester G., Pascual-BorràsM., Ohlin C.A., Rompel A. Inorg. Chem., 58, 2019, 106–113. DOI: https://doi.org/10.1021/acs.inorgchem.8b01740
[7]. Бакеева И.В., Морозова И.В. “Современные нанокомпозитные материалы – органо-неорганические гибридные гели”. Учебное пособие. М., МИТХТ им. М.В. Ломоносова, 2006.
[8]. Wu Q.,Wu W., Wu Y., Li W., Qiao Y., Wang Y., Wang B.. J. Of Molecular Structure, 1157, 2018, 616-620. DOI: https://doi.org/10.1016/j.molstruc.2017.12.082
[9]. Казанский Л.П., Голубев А.М. “Колебательные спектры гетерополианионов различных структурных типов. В сб. Химия соединений Mo (VI) и W(VI)”. Новосибирск: Наука, 1979, 66–84.
[10]. T. G. G. Battye, L. Kontogiannis, O. Johnson, H. R. Powell, A. G. W. Leslie. Acta Cryst., D67, 2011, P. 271-281. DOI: https://doi.org/10.1107/S0907444910048675
[11]. P. R. Evans. Scaling and assessment of data quality. Acta Cryst., D62, 2005, P. 72-82. DOI: https://doi.org/10.1107/S0907444905036693
[12]. G. M. Sheldrick. “Crystalstructure refinement with SHELXL”. Acta Cryst., C71, 2015, P. 3-8. DOI: https://doi.org/10.1107/S2053229614024218